Photocatalytic toluene oxidation with nickel-mediated cascaded active units over Ni/Bi2WO6 monolayers (2024)

Characterization of the prepared samples

A series of Ni/BWO samples with different Ni mass fractions were prepared via a modified one-step solvothermal route²². The schematic diagram is shown in Fig.1a. The actual mass fractions of Ni were determined by Inductively Coupled Plasma Mass Spectrometry (ICP-MS) to be 0.9%, 1.8%, and 2.6% (Supplementary Table1). The corresponding samples were named as 0.9 Ni/BWO, 1.8 Ni/BWO, and 2.6 Ni/BWO, respectively. The X-ray diffraction (XRD) patterns (Fig.1b (2θ from 25° to 35°) and Supplementary Fig.1 (2θ from 5° to 70°)) show that all the samples are well matched with orthorhombic Bi₂WO₆ (JCPDS No. 73-2020; lattice parameters: a = 5.457 Å, b = 5.436 Å, and c = 16.427 Å)^4,23. Interestingly, the XRD peaks shift to higher 2-theta with Ni doping, suggesting the contracted lattice of BWO, i.e., the substitution of Bi or W atoms by Ni atoms²⁴. Fourier transform infrared (FT-IR) spectra (Fig.1c) provide further microstructural details of these samples. The characteristic peaks of the O-W-O and W-O-W stretching vibrations at 736 and 577 cm⁻¹ are gradually weakened with the introduction of Ni²⁵, especially the O-W-O stretching peaks shift to low wavenumbers, indicating that some of the W atoms are substituted by Ni atoms. Two formed peaks at 955 and 665 cm⁻¹ are attributed to the short W=O and Ni-O stretching vibrations^25,26, respectively, suggesting that the ordered crystal structure of BWO is disrupted and part of the lattice oxygen atoms are lost, yielding numerous coordinatively unsaturated W atoms. Raman spectra (Fig.1d) also show a characteristic peak at 782 cm⁻¹ assigned to the antisymmetric A_g mode of O-W-O.^4,27 The vibrational intensity becomes weaker with Ni doping, also indicating the substitution of W atoms by Ni atoms. Consistent with the FTIR results, the symmetric stretching peak of the short terminal W = O at 955 cm⁻¹ is observed after the introduction of Ni^4,27,28, illustrating that Ni breaks the ordered crystal arrangement of BWO accompanied by the formation of the O_V and coordinatively unsaturated W atoms. O_Vs have a spatial separation effect favoring the formation of FLPs^14,16.

The morphology and structure of the as-prepared samples were studied by field-emission scanning electron microscopy (SEM), transmission electron microscopy (TEM), and atomic force microscopy (AFM). Supplementary Fig.2 illustrates that both 1.8 Ni/BWO and BWO samples exhibit similar nanosheet morphology, with an average thickness of approximately 1.5 nm (Fig.1e and Supplementary Fig.3). This measured thickness closely aligns with the interlayer spacing along the c-axis of orthorhombic Bi₂WO₆²⁹, indicating the successful synthesis of monolayer nanosheets, independent of the introduction of Ni atoms. These ultrathin nanosheets are well-resolved in subsequent low-magnified TEM images (Supplementary Fig.4a: BWO, Fig.1f: 1.8 Ni/BWO) and show a lattice spacing of 0.27 nm corresponding to the {002} planes of Bi₂WO₆^4,29,30 Notably, in contrast to the long-range ordered structure of the BWO sample (Supplementary Fig.4b), lattice-disordered regions (highlighted by dotted lines) are observed within the 1.8 Ni/BWO counterpart (Fig.1g). This observation suggests that the incorporation of Ni elements introduces a high density of surface defects within the Bi₂WO₆ nanosheets, which is potentially beneficial for the formation of FLPs³¹ The specific surface areas of the 1.8 Ni/BWO and BWO nanosheets are relatively close (Supplementary Fig.5). These results demonstrate that the introduction of Ni atoms leads to the emergence of surface defects in the Ni/BWO sample, with only a minor effect on the morphology. In the absence of Ni, Bi₂WO₆ with good crystallinity is formed by the combination of [BiO]⁺–[WO₄]²⁻–[BiO]⁺ structural units^29,32 resulting in saturation of the coordination of most surface metal atoms in BWO. These CLPs, based on adjacent lattice atoms of Bi₂WO₆, are generally difficult to activate C–H bonds. Upon the introduction of Ni, the long-range ordered [BiO]⁺–[WO₄]²⁻–[BiO]⁺ structural units are disrupted, leading to the formation of surface O vacancies and coordinatively unsaturated metal atoms. This disruption may spatially separate surface O species and metal atoms, potentially serving as FLPs. This structural insight suggests the possibility of the formation of CAUs, including FLPs and CUSs.

Energy-dispersive spectroscopy (EDS) mapping combined with aberration-corrected scanning transmission electron microscopy (AC-STEM) was utilized to investigate the spatial distribution of Ni atoms and atomic-scale defects (Fig.2a–i). The low-magnification high-angle annular dark field (HAADF, Fig.1a) image and EDS maps (Fig.1b–e) show a hom*ogeneous distribution of incorporated Ni atoms within the 1.8 Ni/BWO nanosheets. Aligning the 1.8 Ni/BWO nanosheet along a [001] zone axis (Supplementary Fig.6) allowed the resolution of metal (Bi and W) and O atoms in the atomic scale integrated differential phase contrast (iDPC) image (Fig.2f). The atomic columns, characterized by bright and dark contrasts, correspond to surface metal cations and O anions, respectively. The magnified view from the white box (Fig.2g) demonstrates intensity fluctuations within the atomic columns. Line profiles (Fig.2h, i) extracted from regions 1 and 2 in Fig.2g confirm that the incorporated Ni atoms replace W/Bi atoms, resulting in a darker contrast and the formation of multiple oxygen vacancies, consistent with earlier observations. These atomic-scale microstructural changes serve as evidence for the creation of O_Vs and FLPs by Ni doping in 1.8 Ni/BWO nanosheets. Some O_Vs are present in the area without Ni dopants. These may be attributed to the spontaneous formation of O_Vs on Bi₂WO₆ monolayer nanosheets.

The surface chemical states of each element were determined by X-ray photoelectron spectroscopy (XPS) spectra. W 4f XPS spectra (Fig. 3a) have two main peaks at 35.8 and 38.0 eV, which are attributed to the 4f_7/2 and 4f_5/2 of W⁶⁺. Compared with BWO, two peaks at 35.3 and 37.5 eV assigned to W⁵⁺ are fitted after doping with Ni^4,33, indicating that part of coordinatively saturated W⁶⁺ atoms are mediated to unsaturated W⁵⁺. Detailed fitting results (Supplementary Table2) show that excessive introduction of Ni only reduces the proportion of W atoms and does not induce more unsaturated W. In addition, Fig.3b exhibits similar characteristic peaks of Bi³⁺ for all the samples³⁴. Three O species are fitted in the O 1s XPS spectra (Supplementary Fig.7a) with binding energies of 529.5, 531.0, and 532.1 eV, corresponding to the lattice oxygen (O_L), O_V and hydroxyl groups (O_OH), respectively^35,36. The O_L ratio (Supplementary Table3) decreases after Ni doping, confirming that part of the lattice oxygen atoms are lost. The formation of O_V is also confirmed by the EPR spectra (Fig.3c)^27,35,37. Interestingly, the characteristic Ni 2p XPS signal (Supplementary Fig.7b) cannot be detected³⁸, but its signal is recorded utilizing cluster etching to remove the surface atoms of 1.8 Ni/BWO (Supplementary Fig.7c). Thus, Ni is doped into the crystal lattice of BWO rather than into the surface. When the Ni is loaded onto the surface of BWO by photo-deposition, the Ni XPS signal is recorded, which also confirms the above view (Supplementary Fig.8).

The fine structure change was analyzed by X-ray absorption fine structure (XAFS) spectroscopy. BWO and 1.8 Ni/BWO both exhibit similar absorption curves in the W L₃-edge XANES spectra (Supplementary Fig.9a). The main peak intensity for 1.8 Ni/BWO is reduced in the extended X-ray absorption fine structure (EXAFS) spectra (Fig.3d) showing that the ordered lattice arrangement of W is broken after doping with Ni^4,39. The peaks in the correlation distance of 1–2 Å are attributed to the signal of W-O, and the peaks in the range of 2.5–3 Å are correspond to the distance between two W atoms^39,40. After doping with Ni ions, the peaks in the range of 2.5–3 Å are split into two peaks, manifesting the replacement of W by Ni. Meanwhile, the coordination number of W atoms decreases for the 1.8 Ni/BWO (Supplementary Fig.9b and Supplementary Table4). The substitution of W by Ni atoms induces the loss of some lattice O atoms, which would produce unsaturated W atoms and make the spatial separation of surface metal atoms and O species around Ni atoms, facilitating the formation of FLPs. Since the unsaturated W atoms and FLPs are both mediated by Ni dopants, they should be easily cascaded into an active unit, thus forming CAUs.

To better illustrate the construction of CAUs, the structure models of Ni/BWO were simulated and optimized by DFT calculation. According to the experimental results, we established the structure models of BWO (001) and Ni/BWO (001), while the BWO (010) and Ni/BWO (010) were also simulated for comparison. As shown in Supplementary Fig.10a–h, the optimized structure model of BWO (010) and Ni/BWO (010) consists of [BiO]⁺–[WO₄]²⁻–[BiO]⁺ links in the longitudinal direction from the side view. The top layer consists of Bi atoms, while Ni atoms are doped into the secondary layer. For the BWO (001) and Ni/BWO (001) models, the links of [BiO]⁺–[WO₄]²⁻–[BiO]⁺ are in a landscape orientation (Supplementary Fig.11a–h). The top layer consists of O atoms and the secondary layer of metal atoms. In addition, the charge density differences shown in Fig.3e show that Ni has a higher electron density while the electron density of Bi atoms around Ni is reduced. This is attributed to the surface charge rearrangement as the substitution of W atoms by Ni atoms. The O_V formation energies on the (010) and (001) faces of pristine BWO and Ni/BWO are shown in Fig.3f. The O_V formation energies on the (010) and (001) faces of pristine BWO are 0.87 and 0.39 eV, respectively, while they change to −1.00 and −1.11 eV after Ni doping. These results confirm that the formation of O_V is easier on BWO (001) and that Ni dopants apparently facilitate the formation of O_V, which is consistent with the results of experiments.

It’s worth noting that the surface microstructures of pristine BWO and Ni/BWO have some differences. As shown in Fig.3g, h and Supplementary Fig.10c, d, the Ni atoms are doped in the secondary metal layer of the (010) surface, so the induced O_V is difficult to make the spatial separation of Bi and O atoms on the top layer. Therefore, FLPs sites are hardly formed on the Ni/BWO (010). Since the W atoms are in the interior, it is difficult to form the CAUs on the (010) facet of Ni/BWO. Interestingly, CAUs containing FLPs and unsaturated W atoms can be formed on the Ni/BWO (001) surface. As shown in Fig.3i, j and Supplementary Fig.11c, d, when the W atoms are replaced by Ni atoms, the lattice distortion, and O_V are formed, which causes the nearby Bi and O atoms to separate in space, forming FLPs. These acid and base sites in the FLPs are not directly linked and thus provide catalytic active centers for activation of the C–H bonds. Meanwhile, unsaturated W atoms are also formed through the mediation of Ni dopant. Moreover, although O_Vs are formed on pristine BWO (010) and (001) faces (Supplementary Fig.10 e, f and Supplementary Fig.11 e, f), the spatial separation of Bi and O atoms is difficult without Ni dopant. The formation of CAUs requires Ni dopants as switches. The Bi atoms around Ni dopants have different electron densities (Supplementary Fig.12), which may be more active than those on pristine BWO¹⁶.

Photocatalytic oxidation of toluene (TL)

The series of samples were used for the photocatalytic oxidation of TL. Figure4a shows that the performance for the photocatalytic TL oxidation is significantly improved after the introduction of Ni. Especially, 1.8 Ni/BWO exhibits the highest conversion rate of TL (4560 μmol g⁻¹ h⁻¹) which is 4.5 times higher than BWO (1020 μmol g⁻¹ h⁻¹). The nanosheet thickness, specific surface area, and energy band structure (Supplementary Fig.13, 14) of 1.8 Ni/BWO and BWO are similar, thus the different performance is attributed to the construction of CAUs. To better compare the important role of CAUs, BWO-bulk, BWO-Ov, Ni/BWO-surface, and BiOCl were prepared. The characterization details are shown in Supplementary Figs.16–18. BWO-bulk only shows the TL conversion rate of 200 μmol g⁻¹ h⁻¹, highlighting the structural advantage of the monolayer nanosheet. When O_V is induced on BWO by heat treatment, the TL conversion rate of BWO-O_V is improved to 1320 μmol g⁻¹ h⁻¹, confirming that O_V promotes the photocatalytic oxidation of TL. However, the O_V induced by heat treatment is random and the formation of CAUs is difficult without Ni dopant according to the DFT results, causing a low improvement of catalytic performance. When the Ni is loaded on the surface of BWO, there are almost no O_v and unsaturated W as well as FLPs. Accordingly, the Ni/BWO-surface shows a TL conversion rate of 1020 μmol g⁻¹ h⁻¹, confirming the close correlation between the TL oxidation performance and the CAUs. In addition, BiOCl with O_V exhibits only 90 μmol g⁻¹ h⁻¹ conversion rate of TL, also indicating that only Bi atoms and O_V cannot realize the effective TL oxidation. There is a synergistic effect between surface FLPs and unsaturated W atoms, which significantly promotes the photocatalytic oxidation of TL.

The apparent quantum efficiencies (AQE) of these samples are shown in Supplementary Table5. Typical 1.8Ni/BWO shows the highest AQE of 6.01% with a turnover frequency (TOF) about 2.2 h⁻¹. Figure4b shows that the main product for the TL oxidation over 1.8Ni/BWO is benzaldehyde (BD). A small number of benzyl alcohol (BA) could be detected at the primary stage. As the reaction time increases, these few BA molecules are further converted to BD. The selectivity of benzaldehyde has consistently been maintained at over 90%, even under the conditions of high toluene conversion (Supplementary Fig.19a and b). Upon complete conversion of TL, BD is further oxidized to BAC. Interestingly, the further oxidation of BD to BAC is more pronounced on BWO (Fig.4c), possibly due to the presence of CAUs promoting the conversion of the oxidation product to BD and suppressing the further oxidation of BD to BAC in the presence of TL. From the results of gas chromatography (Supplementary Fig.19c and d), no other liquid and gas phase products are detected. No benzaldehyde is produced in the dark, regardless of temperature (Supplementary Fig.20a). It confirms that the oxidation of toluene is driven by light. The results of five cycle experiments (Supplementary Fig.20b), XRD pattern (Supplementary Fig.21a), TEM, and element mapping images (Supplementary Fig.21b, c, and d) suggest a high stability of 1.8Ni/BWO. This photocatalyst also shows good conversion for the oxidation of other toluene derivatives (Supplementary Table6). The construction of Ni mediated CAUs is a highly efficiency strategy to improve the photocatalytic performance of TL oxidation compared to the reported studies (Supplementary Table7).

Study on structure-activity relationship

To understand the better performance of the 1.8 Ni/BWO, further experiments and DFT calculations were investigated. In situ Diffuse Reflectance Infrared Fourier Transform (DRIFT) spectroscopy was applied to trace the adsorption process of O₂ and TL molecules. Figure5a shows two absorption peaks appeared at 1476 cm⁻¹ and 1290 cm⁻¹, corresponding to the vibrational peaks of adsorbed oxygen and the vibration model of superoxide O–O in surface-coordinated oxygen complexes, respectively^41,42. In comparison, BWO exhibits a weaker signal (Fig.5b), suggesting that the CAUs of 1.8 Ni/BWO enhance the adsorption of O₂. As the calculated adsorption energies of O₂ on unsaturated Bi, Ni, and W sites are 0.31, 0.14, and −0.10 eV, (Supplementary Table8) respectively, it tends to be adsorbed on unsaturated W atoms rather than polar FLPs. Thus, unsaturated W atoms are considered to be the active centers for the activation of O₂ molecules, as discussed definitely in the recent study³⁵. O₂-TPD spectra (Fig.5c) also shows that 1.8 Ni/BWO has a desorption peak at around 370 °C, which is related to the chemical adsorbed oxygen species, corresponding to the O₂⁻ and O₂²⁻ adsorbed on unsaturated W atoms⁴³. Ni-induced the coordination-unsaturated W atoms can facilitate chemisorption of O₂, resulting in the formation of activated oxygen species on the surface. This is expected to play an important role in the subsequent oxygen transfer process.

Figure5d further provides evidence for the activation of C–H. We hypothesize that the signal of TL on KBr is similar to the signal of free TL molecules. The signal of TL on KBr is still very weak after adsorption for 25 min. However, the signal peak intensity gradually increased with time on 1.8 Ni/BWO, illustrating the accumulation of the adsorbed TL. The peaks at 3084, 3064, and 3028 cm⁻¹ are attributed to the stretching vibration of the C–H bond of the benzene ring, while the peaks at 2958, 2927, and 2854 cm⁻¹ are the stretching vibration of –CH₃^3,44. Obviously, the characteristic stretching vibration peaks of the C–H bond in the benzene ring have an unnoticeable shift while the peaks of the –CH₃ stretching vibration gradually shift to 2944, 2920, and 2875 cm⁻¹, respectively, demonstrating that –CH₃ is chemisorbed and activated. In comparison, the activation of the C–H bonds on BWO is weak (Fig.5g). This result implies that the generated surface FLPs are active centers for chemisorbing C–H bonds. In addition, the force constant (k) quantization (Supplementary Table9) shows two C–H bonds are obviously weakened while one C–H bond is strengthened⁴⁵, indicating that the products on FLPs may be easily converted to BD.

The photocatalytic oxidation process of TL and the possible intermediates were traced by in situ DRIFTS under visible light. As shown in Fig.5e, the characteristic peaks of the –OH stretching vibration (1230 cm⁻¹), –OH in-plane bending vibration (1314, 1340 cm⁻¹), and –C=O stretching vibration (1646, 1680 cm⁻¹) are recorded, indicating the formation of BA and BD^44,46,47. Considering that the -C = O bond of the carboxyl group also has a characteristic peak at 1680 cm^{−1 48}, we speculate that some BAC may be formed gradually over time. The –C = O stretching vibration peaks grow rapidly, indicating that BD is the main product during the photocatalytic process. The further oxidation of BAC to CO₂ cannot proceed because no signal of CO₂ was detected at the wavenumber 2200-2400 cm⁻¹ (Supplementary Fig.22)⁴⁷. Moreover, the vibrational signal of chemical adsorbed oxygen complexes (1290 cm⁻¹) gradually becomes weaker, demonstrating that there is a oxygen transfer process. This process is difficult to observe using BWO as a photocatalyst due to the lack of CAUs (Fig.5g). The oxygen transfer process is further confirmed by the ¹⁸O₂ isotope-labeling experiment. As shown in Fig.5f, when using ¹⁸O₂ as oxygen source, 80% of the BD molecules are labeled by ¹⁸O, suggesting that most of the benzaldehyde’s O atoms come from O₂. Considering the difficulty for lattice oxygen on tungsten (W) to participate in reactions (Supplementary Fig.23), the remaining O atoms are considered to be the chemical adsorbed oxygen species on unsaturated W atoms when the sample is exposed to air, consistent with the results of in situ DRIFTS and O₂-TPD. This result confirms that CUSs would adsorb O₂ molecules to form chemical adsorbed oxygen species and establish a special process for transferring oxygen on the surface.

In addition, the active free radicals during the reaction are investigated by Electron Paramagnetic Resonance (EPR) technology. Supplementary Fig.24 shows all prepared samples exhibit the carbon-centered (^*C₇H₇) and •O₂⁻ radical signals due to the deprotonation of TL by photogenerated holes and the reduction of O₂ by photogenerated electrons^4,49,50, No signals are detected in the dark, indicating the necessary condition of light. 1.8 Ni/BWO shows the strongest EPR signal which is consistent with its best performance in TL oxidation. The reason is that the number of defects and active sites induced varies with different mass fractions of Ni. When the mass fraction of Ni is 1.8%, it produces the highest concentration for W⁵⁺ and FLPs (Fig.3), which is favorable for the adsorption and activation of reactants. Surface defects also facilitate the separation of photogenerated electron-hole pairs (Supplementary Fig.25)⁵¹, thereby enhancing photocatalytic performance. The free radical quenching experiments reveal that the deprotonation of TL by photogenerated holes is the key step for the oxidation of TL and •O₂⁻ radicals are considered as one of the active O species in the subsequent oxidation process and another O transfer pathway also exists (Supplementary Fig.24c).

The DFT simulations are also performed to reveal the surface O transfer process based on the optimized Ni/BWO (001) model. As shown in Fig.6a, structure I is the model of Ni/BWO (001). When the O₂ molecule is added, this model tends to adsorb the O₂ molecule with a binding energy of −0.1 eV (model II). The O₂ molecule is then activated via two W···O coordination. On the one hand, some of these activated O₂ molecules can be directly reduced to •O₂⁻ radical species by the photo-excited electrons (Supplementary Fig.24b). On the other hand, as the distance between two O atoms is stretched by W atoms in Fig.6a TS1, the chemical adsorbed oxygen species are eventually broken (model III). Interestingly, the O atoms from the broken chemical adsorbed oxygen species in model III can easily deliver to Ni atoms (TS2). The energy barrier for this surface O delivery process from model III to model IV is sufficiently low (0.59 eV) and easy to overcome. The transferred active O atoms can be used for the formation of BD and H₂O. This surface active O transfer channel is more efficient because it occurs in a CAU.

Meanwhile, the calculated activation path of the C–H bond in TL on Ni/BWO (001) is compared with that on Ni/BWO (010), BWO-O_V (010) and BWO-O_V (001) in Fig.6b. “2^* + O_V” represents those two active atoms around O_V selected to combine with the C and H atoms of TL. The subsequent ^*+^*C₇H₈ (TL) dehydrogenation to ^*C₇H₇-H^* undergoes a transition state (TS). The intermediate ^*C₇H₇ has been confirmed by EPR experiments (Supplementary Fig.24a). The corresponding geometries and energies are shown in Fig.6c. The energy barriers to be overcome for the dehydrogenation of toluene on Ni/BWO (001) (TS₄), Ni/BWO (010) (TS₃), BWO-OV (001) (TS₂), and BWO-OV (010) (TS₁) are 0.23, 0.28, 1.02, and 1.16 eV, respectively. The energy barriers on BWO-OV (001) and BWO-OV (010) are significantly lower than those on Ni/BWO (001) and Ni/BWO (010), indicating that the Bi and O atoms on Ni/BWO (001) and Ni/BWO (010) are more active due to the regulation of the Ni dopants. Particularly, the TL molecules adsorbed on Ni/BWO (001) are easily dehydrogenated due to the formation of Bi···C and O···H coordination between the FLPs and the C–H bond. The transient charge density difference image of TS4 (Fig.6d) shows that the Bi···C and O···H coordination cause the electrons of H in C–H bonds to transfer to O atoms and the electrons of Bi to shift to C, resulting in the effective activation of C–H bonds. Furthermore, since doping can lead to a redistribution of charge around neighboring atoms⁵², we considered the influence of potential surrounding sites (such as Ni and Bi site) and found that the current FLP adsorption system for the C–H has the lowest energy (Supplementary Fig.26a). The Bi···C and O···H coordination as bridges for the transfer of photogenerated holes from the Bi and O atoms to C–H bonds, which significantly promotes the deprotonation of the C–H bonds. After the dehydrogenation of TL, the O atoms in the FLPs could combine with H atoms to form surface –OH (Supplementary Fig.26b). The corresponding valence states of the spatially separated Bi and O atoms show little change (Supplementary Table10) and can continue to be used as FLPs to dehydrogenate the ^*C₇H₇ intermediate. More surface hydroxyl groups on 1.8 Ni/BWO (XPS results) also indicate the highest levels of FLPs on 1.8 Ni/BWO, which promotes the activation and dehydrogenation of the C–H bond. The surface –OH combines with the H atom in the C–H bond to form a desorbed H₂O molecule, leaving a lowly coordinated Ni atom and the ^*C₇H₆ intermediate. The delivered O atoms in model IV of Fig.6a would further transfer to the ^*C₇H₆ intermediate to form benzaldehyde. The desorption energies of benzaldehyde on Ni/BWO-(001) and BWO-(001) are 0.41 and 0.69 eV (Supplementary Fig.26d), respectively, indicating the easier desorption of benzaldehyde on Ni/BWO-(001). This provides a reasonable explanation for the better selectivity of benzaldehyde on 1.8 Ni/BWO than that on BWO.

Based on the experimental results and the DFT simulations, we find a special surface pathway for the photocatalytic toluene oxidation induced by the Ni dopant mediated CAUs (Fig.6e), which is different from the traditional photocatalytic mechanism (Supplementary Fig.27). Firstly, the O₂ and TL molecules would be activated on the unsaturated W atoms and FLPs, respectively. Then, some of the activated O₂ and TL molecules can be converted to •O₂^- and ^*C₇H₇ radicals under the attack of photogenerated electrons and holes. Moreover, some activated oxygen species can be directly broken on unsaturated W atoms, while a C–H bond in the –CH₃ group is broken with the formation of ^*C₇H₇ intermediates and a surface hydroxyl group. The ^*C₇H₇ intermediates can be further oxidized to ^*C₇H₆ and release an H₂O molecule by photogenerated h⁺ and •O₂⁻ radicals. Finally, active O species are efficiently transferred in CAUs to oxygenate the ^*C₇H₆ intermediates to BD and replenish the O consumption of dehydration for starting the next cycle.

In summary, we have successfully developed monolayer Ni-doped B₂WO₆ nanosheets (Ni/BWO) as a highly efficient photocatalyst for the selective oxidation of toluene to benzaldehyde. The experimental characterization clarified that Ni dopants mediated cascaded active units (CAUs) at the atomic scale, including unsaturated metal W atoms and spatially separated Bi and O atoms as FLP sites. The FLPs sites are the active centers for adsorbing the C–H bonds of toluene via Bi···C and O···H coordination, while O₂ is adsorbed on the unsaturated metal W sites. It builds bridges for the effective transfer of photogenerated carriers, promoting the subsequent process of toluene oxidation by light-induced active species. In addition, the surface FLPs and unsaturated W sites also establish a special route for the oxidation of C–H bonds, including the dehydrogenation of C–H bonds, the activation of O₂, and the efficient delivery of surface O. Therefore, the representative 1.8 Ni/BWO exhibits a significantly enhanced toluene conversion rate of 4560 μmol g⁻¹ h⁻¹. This work presents an experimental and theoretical basis for designing CAUs with a synergistic effect via Ni doping.